Injection lasers

ABSTRACT

A double heterostructure injection laser has its active layer close to the surface. A rib protruding from that surface provides lateral optical confinement of laser radiation propagating in the active layer under the rib.

This is a continuation of application Ser. No. 734,687 filed Oct. 22, 1976, now abandoned, which was a divisional application of application Ser. No. 646,115 filed Jan. 2, 1976 which issued as U.S. Pat. No. 4,011,113 on Mar. 8, 1977.

This invention relates to lasers, and in particular to the provision of lateral confinement of light within the laser cavity of double heterostructure injection lasers.

According to the present invention there is provided a double heterostructure injection laser wherein the active region lies so close to the semiconductor surface that lateral optical guiding of radiation within the optical cavity is realised at least in part by providing said surface with a protruding rib overlying the laser active region, which surface, in each of the regions flanking the rib, is bounded by a lower refractive index medium.

In our United Kingdom Pat. No. 1,273,284 (G.H.B. Thompson) there is described a way of obtaining current confinement in a heterostructure injection laser by arranging for the p-n junction to extend into the lower band gap material for only a short portion of its length. Under these conditions the current flow across the p-n junction is confined to the region where it is in the lower band gap material. This current confinement is accompanied by optical confinement provided by the heterojunctions. The optical confinement provided by heterojunctions can be relatively strong, but only in one of the described embodiments does the heterojunction fully encircle the active region providing strong optical confinement extending all round the active region. This invention discloses an alternative method of achieving lateral optical confinement by arranging for the active region to lie so close to the surface of the semiconductor material that the requisite optical guidance can be provided by a protruding rib of semiconductor material.

Accordingly the invention also provides a double heterostructure injection laser whose active region is contained in a layer bounded on both sides by lower refractive index and larger band gap layers, wherein the p-n junction of the laser extends in the larger band gap material except for a narrow strip extending in the direction of the optical axis of the laser cavity from one end face thereof to the other in which the p-n junction is bounded on at least one side by the lower band gap material of the active region thereby providing current confinement, and wherein optical confinement in the lateral direction is provided by the semiconductive material of the laser having a surface profile which includes a protruding rib overlying the strip which rib is flanked by regions where the semiconductive material is bounded by an interface with a lower refractive index medium which interface is so close to the layer containing the active region that the laser radiation preferentially propagates in the region under the rib.

The invention further provides a method of making a double heterostructure injection laser including the steps of forming a double heterostructure with a layer bounded on both sides by layers of the same conductivity type but larger band gap, the upper of said larger bandgap layers having a thickness not large compared with the wavelength of the laser radiation in said upper layer, of growing an epitaxial layer of opposite conductivity type on said upper layer using a conductivity type determining dopant of greater mobility and in greater concentration than used in the provision of the underlying layers of the double heterostructure, of selectively removing all of said epitaxial layer with the exception of a stripe extending in a direction normal to a cleavage plane, and of heating the structure so as to promote diffusion of the greater mobility dopant until the p-n junction beneath the stripe is translated into the smaller band gap layer of the double heterostructure.

There follows a description of the manufacture of a GaAlAs double heterostructure laser embodying the invention in a preferred form. The description refers to the accompanying drawings in which:

FIG. 1 depicts a schematic view of a cross section through the laser, and

FIG. 2 depicts the band diagrams for a modified version of the laser of FIG. 1.

Referring to FIG. 1 a succession of three n-type layers 1, 2, 3, and then two p-type layers 4 and 5 are epitaxially grown upon an n-type GaAs substrate 6. The middle n-type layer 2 is of smaller band gap than layers 1 and 3. Layers 2 and 3 are thinner than layer 1. Layer 2 should have a carrier concentration (n-type) approximately equal to the electron concentration injected into that portion which forms the active layer of the laser, when the laser reaches threshold (about 1 to 2×10¹⁸ cm⁻³). This minimizes transverse diffusion effects. Layer 4 is required to have a greater carrier concentration and larger band gap than layer 2, while layer 5 is a GaAs provided for the facilitating of making an electrical contact with the p-type material.

A central strip of layer 5 is masked so that the remainder of layers 4 and 5 can be selectively etched away to leave a projecting rib 7. The alignment of the mask is such that the rib extends in a direction normal to a cleavage plane. The etch is required to terminate at p-n junction forming the boundary between layers 3 and 4 and therefore it is convenient to make use of a self limiting electrochemical etch for this process. Alternatively the requisite material may be removed by anodic etching.

After the etch, the slice is heated to cause the p-type dopant of layer 4 to diffuse into the underlying n-type layers 2 and 3 so as to translate the p-n junction front 8 into layer 2. For this purpose layer 4 is required to have a greater carrier concentration than that of the underlying layers 2 and 3, and its dopant mobility must also be greater. Another process step is the provision of metallisation contact layers 9 and 10 on the p-type and n-type sides of the device. A dielectric layer 11 is required under contact 9 to prevent it from short-circuiting the p-n junction. This layer 11 may be provided by conventional passivation layer deposition techniques, but this will normally involve the removal of the initial mask covering the rib, and hence re-masking will be required to enable the passivation to be removed from the top of the rib to expose it to the metallisation 9. This remasking requires critical alignment in the case of fine width ribs, and hence it would be preferred to deposit the insulation by some method which makes use either of the mask used for creating the rib of the rib itself and hence avoids the necessity for remasking. One possible method is to create the layer 11 by anodisation. The layer so created must be capable of withstanding the temperatures involved in the subsequent diffusion of the p-type dopant through layer 3 into layer 2.

In order to obtain the maximum control of both the depth and the lateral spread of the diffusion, this diffusion should be arranged to be as shallow as possible. This means that the n-type layer 3 should be thin. The limit on its thinness is set by the allowable proximity of the optical guiding layer 2 to the interface between layer 3 and the dielectric layer 11. This must be decided in terms of the interaction of this interface with the guided propagation of light. Provided that the refractive index of the dielectric layer 11 is lower than that of layer 4 this interaction is favourable because the proximity of the interface tends to exclude the guided light from the regions under the interface and hence concentrate it under the rib. Only when the exclusion becomes so strong that higher order transverse modes can be set up under the rib can the interface be considered to be too close. The single mode condition depends upon the width of the rib in such a way that the narrower the rib is, the greater is the amount of material that can be removed from the regions flanking the rib before higher transverse modes are set up. This means that with a narrower rib the layer 4 can be thinner, with the result that the p-type dopant has a shorter distance to diffuse through, and hence the lateral diffusion is reduced and the junction width corresponds more nearly to the width of the rib. These factors co-operate in such a way that a rib width of about 1 μm is not impractical in a device having a layer 4 thickness in the region of 0.1 to 0.2 μm.

The mobile p-type dopant for layer 4 is conveniently zinc which has a significantly greater mobility than tin or tellurium which may be used as the dopant for the n-type layers. Layers 2 and 3 are lightly doped compared with layer 4 so that the diffusion of the zinc into layers 2 and 3 will readily result in a conversion of conductivity type. Typically layer 4 has a carrier concentration of 3 to 4×10¹⁸ cm⁻³ while layers 2 and 3 have 1 to 2×10¹⁸ cm⁻³. Layer 1 has a slightly higher carrier concentration of about 2×10¹⁸ cm⁻³ in order to minimise the risk of the p-n junction penetrating into it. Layer 5 has a high carrier concentration, typically of about 10¹⁹ cm⁻³, in order to minimise chmic contact resistance; high impurity mobility is not desirable and hence germanium or magnesium may conveniently be used as the dopant.

The thickness requirements and compositions for layers 1 and 2 are the same as those of conventional double heterostructure lasers. Thus layer 1 is typically 1 μm thick Ga₀.7 Al₀.3 As and layer 2, 0.2 μm thick GaAs. Typically layers 3 and 4 have the same percentage of AlAs as layer 1. Layer 4 is typically about 1 μm thick; and for a 2 μm rib width, layer 3 is preferably about 0.2 μm thick.

Layer 2 may alternatively be made of GaAlAs provided that its percentage of aluminium is much less than that of layers 1, 3 and 4.

Three layers may be used in place of a single layer 2 so as to produce a more complex structure in which the functions of electrical confinement and optical guidance are substantially separated. In this instance the middle layer of the three is made of smaller band gap material than the two flanking layers which in their turn are made of smaller band gap material than that of layers 1 and 2. The advantages of such a five layer heterostructure are explained in greater detail in our United Kingdom Pat. No. 1,263,835 (G.H.B. Thompson) to which attention is directed.

Preferably the zinc diffusion should be terminated when the p-n junction lies in the active layer 23 which is the middle, lowest band gap, layer of the five layers. This is the condition depicted in the bandgap diagram of FIG. 2a. If however the diffusion does not go deep enough so that the p-n junction comes to rest in the intermediate band gap material layer 22 immediately above the active layer, the condition is as depicted in the band gap diagram of FIG. 2b. In this case an additional voltage δV is required to drive the injected electrons over the potential barrier and into the active layer. A rough calculation, assuming a carrier concentration in the active layer of about 2×10¹⁸ cm⁻³ at laser threshold, indicates that this additional voltage amounts to about 20 mV for an AlAs step of 16% at the heterojunction between layer 21 concentration at the heterojunctions bordering and the active layer 22. An analogous situation (FIG. 2c) occurs if the diffusion is so deep that the p-n junction comes to rest in the layer 24 immediately beneath the active layer. In this instance the injected holes require an additional voltage δV to tunnel under the potential barrier in the n-type part of layer 24. Making the same assumptions as before, it is calculated that for an AlAs step of 10% the voltage drop is less than 20 mV. For a voltage drop of 100 mV it is calculated that both the above AlAs steps could be increased by about 6%.

It is to be understood that the foregoing description of specific examples of this invention is made by way of example only and is not to be considered as a limitation on its scope. 

What is claimed is:
 1. In a double heterostructure injection laser said double heterostructure comprising an active layer of high refractive index semiconductor material bounded by a first and second layer of low refractive index semiconductor material, wherein the improvement comprises:a rib of semiconductor material formed on said second layer overlying said active region, a third layer of material disposed adjacent said rib on the surface of said second layer, said rib extending from said second layer and protruding through said third layer, said rib having a higher refractive index than the refractive index of said third layer; said second layer having a thickness not large compared with the wavelength of the laser radiation in said second layer, said thickness being about 0.2 micron.
 2. In a double heterostructure injection laser said double heterostructure comprising an active layer of high refractive index semiconductor material bounded by a first and second layer of low refractive index semiconductor material, wherein the improvement comprises:a rib of semiconductor material formed on the surface of said second layer overlying said active region, a third layer of material disposed adjacent said rib on the surface of said second layer, said rib extending from said surface and protruding through said third layer of material, said rib having a higher index of refraction than the refractive index of said third layer; said second layer having a thickness of about 0.2 microns, whereby said active region is formed sufficiently close to said surface of said second layer so that the laser radiation preferentially propagates in the region under said rib.
 3. A double heterostructure injection laser as described in claim 2 further including a thin elongated region having P-type conductivity formed under said rib and extending inwardly through said second layer and partially into said active layer, said active layer having an N-type conductivity, thereby forming a PN-junction bounded on at least one side by the high refractive index material of said active region and thereby providing current confinement. 